Electrolyte for lithium secondary batteries and lithium secondary battery including the same

ABSTRACT

Disclosed are an electrolyte for lithium secondary batteries including a lithium salt and a non-aqueous solvent, in which the non-aqueous solvent includes an ether based solvent and a glyme based solvent and a ratio of the ether based solvent to the glyme based solvent is 20:80 to 60:40 based on the total volume of the non-aqueous solvent, and a secondary battery including the same.

TECHNICAL FIELD

The present invention relates to an electrolyte for lithium secondary batteries and a lithium secondary battery including the same. More particularly, the present invention relates to an electrolyte for lithium secondary batteries including a lithium salt and a non-aqueous solvent, in which the non-aqueous solvent includes an ether based solvent and a glyme based solvent and a ratio of the ether based solvent to the glyme based solvent is 20:80 to 60:40 based on a total volume of the non-aqueous solvent, and a lithium secondary battery including the same.

BACKGROUND ART

Demand for lithium secondary batteries as energy sources is rapidly increasing as mobile device technology continues to develop and demand therefor continues to increase. Recently, use of lithium secondary batteries as a power source of electric vehicles (EVs) and hybrid electric vehicles (HEVs) has been realized. Accordingly, research into secondary batteries, which may meet a variety of requirements, is being actively performed. In particular, there is high demand for lithium secondary batteries having high energy density, high discharge voltage, and output stability.

In particular, lithium secondary batteries used in hybrid electric vehicles must exhibit great output in a short time and be used for 10 years or more under harsh conditions of repeated charge and discharge on a daily basis. Therefore, a lithium secondary battery exhibiting superior stability and output characteristics to existing small-sized lithium secondary batteries is required.

In connection with this, existing lithium secondary batteries generally use a lithium cobalt composite oxide having a layered structure, as a cathode and a graphite-based material as an anode. However, LiCoO₂ has advantages such as superior energy density and high-temperature characteristics while having disadvantages such as poor output characteristics. Due to such disadvantages, high output temporarily required at abrupt driving and rapid accelerating is provided from a battery and thus LiCoO₂ is not suitable for use in hybrid electric vehicles (HEV) which require high output. In addition, due to characteristics of a method of preparing LiNiO₂, it is difficult to apply LiNiO₂ to actual production processes at reasonable cost. Furthermore, lithium manganese oxides such as LiMnO₂, LiMn₂O₄, and the like exhibit drawbacks such as poor cycle characteristics and the like.

Accordingly, a method of using a lithium transition metal phosphate as a cathode active material is under study. The lithium transition metal phosphate is widely classified into LixM₂(PO₄)₃ having a NaSICON structure and LiMPO₄ having an olivine structure, and considered as a material having superior stability, when compared with existing LiCoO₂.

A carbon-based active material is mainly used as an anode active material. The carbon-based active material has a very low discharge potential of approximately −3 V, and exhibits extremely reversible charge/discharge behavior due to uniaxial orientation of a graphene layer, thereby exhibiting superior electrode cycle life.

Meanwhile, lithium secondary batteries are prepared by disposing a porous polymer separator between an anode and a cathode, and inserting a non-aqueous electrolyte containing a lithium salt such as LiPF₆ and the like thereinto. Lithium ions of a cathode active material are released and inserted into a carbon layer of an anode during charging, whereas lithium ions of the carbon layer are released and inserted into a cathode active material during discharging. In this regard, a non-aqueous electrolyte between an anode and a cathode functions as a medium in which lithium ions migrate. Such lithium secondary batteries must be basically stable in a range of battery operation voltage and must have ability to transfer ions at a sufficiently fast speed.

As the non-aqueous electrolyte, existing carbonate based solvents were used. However, carbonate based solvents have problems such as decreased ionic conductivity due to increased viscosity.

Therefore, there is an urgent need for technology to resolve the problems.

DISCLOSURE Technical Problem

The present invention aims to address the aforementioned problems of the related art and to achieve technical goals that have long been sought.

As a result of a variety of extensive and intensive studies and experiments, the inventors of the present invention confirmed that, when an electrolyte for secondary batteries including predetermined amounts of a glyme based solvent and an ether based solvent is used as a non-aqueous solvent, desired effects may be accomplished, thus completing the present invention.

Technical Solution

In accordance with one aspect of the present invention, provided is an electrolyte for lithium secondary batteries including a lithium salt and a non-aqueous solvent, in which the non-aqueous solvent includes an ether based solvent and a glyme based solvent and a ratio of the ether based solvent to the glyme based solvent is 20:80 to 60:40 based on a total volume of the non-aqueous solvent.

Generally, carbonate solvents have problems such as low ionic conductivity due to high viscosity. On the other hand, glyme based solvents have larger dipole moment than carbonate based solvents and, thus, may improve migration of lithium ions and dissociation degrees of lithium salts. As a result, a lithium secondary battery including the glyme based solvents may have superior room- and low-temperature output characteristics.

In the present invention, a glyme based solvent means glyme and poly glyme. Particularly, the glyme based solvent may be at least one selected from ethylene glycol dimethyl ether (CH₃OCH₂CH₂OCH₃: monoglyme), diethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₂OCH₃: diglyme), diethylene glycol diethylether (C₂H₅(OCH₂CH₂)₂OC₂H₅), triethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₃OCH₃), triethylene glycol diethylether (C₂H₅(OCH₂CH₂)₃OC₂H₅). In particular, diethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₂OCH₃: diglyme) has a dielectric constant smaller than carbonate based solvents and, as such, may exhibit superior effects.

The ether based solvent may be at least one selected from the group consisting of tetrahydrofuran, 2-methyltetrahydrofuran, dimethyl ether, and dibutyl ether. Particularly, the ether based solvent may be dimethyl ether.

That is, when, in electrolyte the according to the present invention, diethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₂OCH₃:diglyme) as a glyme based solvent is used and dimethyl ether as an ether based solvent is used, effects may be maximized.

When the amount of the glyme based solvent is extremely large, discharge capacity and charge/discharge characteristics may be relatively deteriorated. On the other hand, when the amount of the glyme based solvent is relatively small, desired output effects may not be exhibited. Accordingly, a ratio of the ether based solvent to the glyme based solvent may be 25:75 to 65:45 based on a total volume of the non-aqueous solvent.

The electrolyte may additionally include a carbonate based solvent.

In this case, when a volume of a mixture of the glyme based solvent and the ether based solvent is A and a volume of the carbonate based solvent is B, a ratio of A:B may be 15:85 to 85:15, particularly 20:80 to 80:20, more particularly 80:20, based on a total volume of the electrolyte.

In this case, a volumetric ratio of the glyme based solvent to the ether based solvent may be varied within a defined range. The volumetric ratio of the glyme based solvent to the ether based solvent to carbonate based solvent may be particularly 45:35:20 to 55:25:20, more particularly 45:35:20 or 55:25:20.

When the amount of the carbonate based solvent is extremely large, ionic conductivity of an electrolyte may be undesirably deteriorated due to the carbonate based solvent having high viscosity. In addition, when the amount of the carbonate based solvent is extremely small, a lithium salt does not readily dissolve in an electrolyte and, thus, ionic dissociation may be undesirably deteriorated.

The carbonate based solvent, for example, may be cyclic carbonate. The cyclic carbonate may be at least one of ethylene carbonate (EC), propylene carbonate (PC), 1,2-butylene carbonate, 2,3-butylene carbonate, 1,2-pentylene carbonate, and 2,3-pentylene carbonate.

In addition, the carbonate based solvent may additionally include linear carbonate. The linear carbonate includes at least one of dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), ethyl methyl carbonate (EMC), methyl propyl carbonate (MPC) and ethyl propyl carbonate (EPC). In this case, a mixing ratio of the cyclic carbonate to the linear carbonate may be 1:4 to 4:1 based on the total weight of the carbonate based solvents.

The lithium salt may be at least one selected from the group consisting of LiCl, LiBr, LiI, LiClO₄, LiBF₄, LiB₁₀Cl₁₀, LiPF₆, LiCF₃SO₃, LiCF₃CO₂, LiAsF₆, LiSbF₆, LiPF₆, LiAlCl₄, CH₃SO₃Li, CF₃SO₃Li, (CF₃SO₂)₂NLi, chloroborane lithium, lithium tetraphenyl borate, and imides. In addition, the concentration of the lithium salt in an electrolyte may be 0.5 to 3 M, particularly 0.8 to 2 M.

The present invention provides a lithium secondary battery including the electrolyte for lithium secondary batteries.

The lithium secondary battery may include (i) a cathode including a lithium metal phosphate according to Formula 1 below, as a cathode active material; and

(ii) an anode including amorphous carbon, as an anode active material,

Li_(1+a)M(PO_(4−b))X_(b)  (1)

wherein M is at least one selected from metals of Groups II to XII, X is at least one selected from F, S and N, −0.5≦a≦+0.5, and 0≦b≦0.1.

In particular, the lithium metal phosphate may be lithium iron phosphate, which has an olivine crystal structure, according to Formula 2 below:

Li_(1+a)Fe_(1−x)M′_(x)(PO_(4−b))X_(b)  (2)

wherein M′ is at least one selected from Al, Mg, Ni, Co, Mn, Ti, Ga, Cu, V, Nb, Zr, Ce, In, Zn, and Y, X is at least one selected from F, S and N, −0.5≦a≦+0.5, 0≦x≦0.5, and 0≦b≦0.1.

When values of a, b, and x are outside the above ranges, conductivity is reduced or it is impossible to maintain the olivine structure of the lithium iron phosphate. In addition, rate characteristics are deteriorated or capacity may be reduced.

More particularly, the lithium metal phosphate having the olivine crystal structure may be LiFePO₄, Li(Fe, Mn)PO₄, Li(Fe, Co)PO₄, Li(Fe, Ni)PO₄, or the like, more particularly LiFePO₄.

That is, the lithium secondary battery according to the present invention uses LiFePO₄ as a cathode active material and amorphous carbon as an anode active material, and thus internal resistance increase, which causes low electrical conductivity of LiFePO₄, may be resolved, and superior high-temperature stability and output characteristics may be exhibited.

In addition, when the predetermined electrolyte according to the present invention is applied together, superior room- and low-temperature output characteristics may be exhibited when compared with the case of using a carbonate solvent.

The lithium metal phosphate may be composed of first particles and/or second particles in which first particles are physically aggregated.

An average particle diameter of the first particles may be 1 nanometer to 300 nanometers and an average particle diameter of the second particles may be 1 to 40 micrometers. Particularly, an average particle diameter of the first particles may be 10 nanometers to 100 nanometers and an average particle diameter of the second particles may be 2 and 30 micrometers. More particularly, an average particle diameter of the second particles may be 3 to 15 micrometers.

When an average particle diameter of the first particles is excessively large, desired improvement of ionic conductivity may not be exhibited. On the other hand when an average particle diameter of the first particles is excessively small, it is not easy to manufacture a battery. In addition, when an average particle diameter of the second particles is excessively large, bulk density is reduced. On the other hand when an average particle diameter of the second particles is excessively small, a process may not be effectively performed.

A specific surface area (BET) of the second particles may be 3 m²/g to 40 m²/g.

The lithium iron phosphate having the olivine crystal structure may be covered with, for example, conductive carbon to improve electrical conductivity. In this case, the amount of the conductive carbon may be 0.1 wt % to 10 wt %, particularly 1 wt % to 5 wt % based on the total weight of the cathode active material. When the amount of the conductive carbon is extremely large, the amount of the lithium iron phosphate having an olivine crystal structure is relatively reduced and, as such, total characteristics of a battery are deteriorated. On the other hand, when the amount of the conductive carbon is extremely small, undesirably, electrical conductivity may not be improved.

The conductive carbon may be coated over a surface of each of the first particles and the second particles. For example, the conductive carbon may be coated to a thickness of 0.1 to 100 nanometers over surfaces of the first particles and to a thickness of 1 to 300 nanometers over surfaces of the second particles.

When the first particles are coated with 0.5 to 1.5 wt % of the conductive carbon based on a total weight of the cathode active material, a thickness of the carbon coating layer may be approximately 0.1 to 2.0 nanometers.

In the present invention, the amorphous carbon is a carbon-based compound other than crystalline graphite and for example, may be hard carbon and/or soft carbon. When crystalline graphite is used, decomposition of the electrolyte may undesirably occur.

The amorphous carbon may be prepared through a process including thermal-treatment at 1800° C. or less. For example, the hard carbon may be prepared through thermal decomposition of a phenolic resin or a furan resin and the soft carbon may be prepared through carbonization of coke, needle coke, or pitch.

An XRD spectrum of an anode to which the amorphous carbon was applied is illustrated in FIG. 1.

Each of the hard carbon and soft carbon, or a mixture thereof may be used as an anode active material. For example, in the mixture, the hard carbon and soft carbon may be mixed in a ratio of 5:95 to 95:5 based on the total weight of an anode active material.

Hereinafter, a composition of the lithium secondary battery according to the present invention will be described.

The lithium secondary battery according to the present invention includes a cathode, which is prepared by coating a mixture of the cathode active material, a conductive material, and a binder on a cathode current collector and drying and pressing the coated cathode current collector, and an anode prepared using the same method as that used to manufacture the cathode. In this case, the mixture may further include a filler as desired.

The cathode current collector is generally fabricated to a thickness of 3 micrometers to 500 micrometers. The cathode current collector is not particularly limited so long as it does not cause chemical changes in the fabricated secondary battery and has high conductivity. For example, the cathode current collector may be made of stainless steel, aluminum, nickel, titanium, sintered carbon, or aluminum or stainless steel surface-treated with carbon, nickel, titanium, silver, or the like. The cathode current collector may have fine irregularities at a surface thereof to increase adhesion between the cathode active material and the cathode current collector. In addition, the cathode current collector may be used in any of various forms including films, sheets, foils, nets, porous structures, foams, and non-woven fabrics.

The conductive material is typically added in an amount of 1 wt % to 50 wt % based on a total weight of a mixture including a cathode active material. There is no particular limit as to the conductive material, so long as it does not cause chemical changes in the fabricated battery and has conductivity. Examples of conductive materials include, but are not limited to, graphite such as natural or artificial graphite; carbon black such as carbon black, acetylene black, Ketjen black, channel black, furnace black, lamp black, and thermal black; conductive fibers such as carbon fibers and metallic fibers; metallic powders such as carbon fluoride powder, aluminum powder, and nickel powder; conductive whiskers such as zinc oxide and potassium titanate; conductive metal oxides such as titanium oxide; and polyphenylene derivatives.

The binder is a component assisting in binding between an active material and a conductive material and in binding of the active material to a current collector. The binder may be typically added in an amount of 1 wt % to 50 wt % based on a total weight of a mixture including a cathode active material. Examples of the binder include, but are not limited to, polyvinylidene fluoride, polyvinyl alcohols, carboxymethylcellulose (CMC), starch, hydroxypropylcellulose, regenerated cellulose, polyvinyl pyrrolidone, tetrafluoroethylene, polyethylene, polypropylene, ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, styrene-butadiene rubber, fluorine rubber, and various copolymers.

The filler is optionally used as a component to inhibit cathode expansion. The filler is not particularly limited so long as it is a fibrous material that does not cause chemical changes in the fabricated secondary battery. Examples of the filler include olefin-based polymers such as polyethylene and polypropylene; and fibrous materials such as glass fiber and carbon fiber.

An anode current collector is typically fabricated to a thickness of 3 micrometers to 500 micrometers. The anode current collector is not particularly limited so long as it does not cause chemical changes in the fabricated secondary battery and has conductivity. For example, the anode current collector may be made of copper, stainless steel, aluminum, nickel, titanium, sintered carbon, copper or stainless steel surface-treated with carbon, nickel, titanium, or silver, and aluminum-cadmium alloys. Similar to the cathode current collector, the anode current collector may also have fine irregularities at a surface thereof to enhance adhesion between the anode current collector and the anode active material. In addition, the anode current collector may be used in various forms including films, sheets, foils, nets, porous structures, foams, and non-woven fabrics.

The lithium secondary battery may have a structure in which an electrode assembly, which includes a cathode, an anode, and a separator disposed between the cathode and the anode, is impregnated with the electrolyte.

The separator is disposed between the cathode and the anode and an insulating thin film having high ion permeability and mechanical strength is used as the separator. The separator typically has a pore diameter of 0.01 micrometers to 10 micrometers and a thickness of 5 micrometers to 300 micrometers. As the separator, sheets or non-woven fabrics made of an olefin polymer such as polypropylene, glass fibers or polyethylene, which have chemical resistance and hydrophobicity, are used. When a solid electrolyte such as a polymer is used as the electrolyte, the solid electrolyte may also serve as a separator.

The lithium salt-containing electrolyte is composed of the non-aqueous organic electrolyte as described above and a lithium salt and additionally may include a non-aqueous organic solvent, an organic solid electrolyte, an inorganic solid electrolyte, and the like, but the present invention is not limited thereto.

Examples of the organic solid electrolyte include polyethylene derivatives, polyethylene oxide derivatives, polypropylene oxide derivatives, phosphoric acid ester polymers, agitation lysine, polyester sulfide, polyvinyl alcohols, polyvinylidene fluoride, and polymers containing ionic dissociation groups.

Examples of the inorganic solid electrolyte include nitrides, halides and sulfates of lithium (Li) such as Li₃N, LiI, Li₅NI₂, Li₃N—LiI—LiOH, LiSiO₄, LiSiO₄—LiI—LiOH, Li₂SiS₃, Li₄SiO₄, Li₄SiO₄—LiI—LiOH, and Li₃PO₄—Li₂S—SiS₂.

In addition, in order to improve charge/discharge characteristics and flame retardancy, for example, pyridine, triethylphosphite, triethanolamine, cyclic ether, ethylenediamine, n-glyme, hexa-phosphate tree amide, nitrobenzene derivatives, sulfur, quinone imine dyes, N-substituted oxazolidinone, N,N-substituted imidazolidine, ethylene glycol dialkyl ether, ammonium salts, pyrrole, 2-methoxy ethanol, aluminum trichloride, or the like may be added to the electrolyte. In some cases, in order to impart incombustibility, the electrolyte may further include a halogen-containing solvent such as carbon tetrachloride and ethylene trifluoride. In addition, in order to improve high-temperature storage characteristics, the electrolyte may further include carbon dioxide gas, fluoro-ethylene carbonate (FEC), propene sultone (PRS), or the like.

The present invention provides a battery module including the lithium secondary battery as a unit cell and a battery pack including the battery module.

The battery pack may be used as a power source for devices that require stability at high temperature, long cycle life, and high rate characteristics.

Examples of the devices include electric vehicles, hybrid electric vehicles (HEVs), plug-in hybrid electric vehicles (PHEVs), and the like, and the secondary battery according to the present invention may be desirably used in hybrid electric vehicles due to superior output characteristics thereof.

Recently, research into use of a lithium secondary battery in an energy storage system, in which unused power is converted into physical or chemical energy for storage and when necessary, the converted energy is used as electric energy, is being actively performed.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawing, in which:

FIG. 1 is a graph illustrating an XRD spectrum of an anode to which amorphous carbon is applied;

FIG. 2 is a graph illustrating relative capacity maintenance ratios of lithium secondary batteries according to Experimental Example 1; and

FIG. 3 is a graph illustrating relative capacity maintenance ratios of lithium secondary batteries according to Experimental Example 2.

MODE FOR INVENTION

Now, the present invention will be described in more detail with reference to the following examples. These examples are provided only for illustration of the present invention and should not be construed as limiting the scope and spirit of the present invention.

Example 1

86 wt % of LiFePO₄ as a cathode active material, 8 wt % of Super-P as a conductive material, and 6 wt % of PVdF as a binder were added to NMP to prepare a cathode mixture slurry. The resulting cathode mixture slurry was coated, dried, and pressed over one side of aluminum foil to prepare a cathode.

93.5 wt % of soft carbon as an anode active material, 2 wt % of Super-P as a conductive material, and 3 wt % of SBR as a binder, and 1.5 wt % of a thickener were added to H₂O as a solvent to prepare an anode mixture slurry. The resulting anode mixture slurry was coated, dried, and pressed over one side of copper foil to prepare an anode.

The cathode and the anode were laminated using Celgard™ as a separator to manufacture an electrode assembly. Subsequently, a lithium non-aqueous electrolyte including 1 M LiPF₆ as lithium salt was added to a solvent including ethylene carbonate, dimethoxyethane, and diglyme mixed in a volumetric ratio of 20:25:55 to manufacture a lithium secondary battery.

Example 2

A lithium secondary battery was manufactured in the same manner as in Example 1, except that a lithium non-aqueous electrolyte containing 1 M LiPF₆ as a lithium salt was added to a solvent including ethylene carbonate, dimethoxyethane, and diglyme mixed in a volumetric ratio of 20:35:45.

Comparative Example 1

A lithium secondary battery was manufactured in the same manner as in Example 1, except that a lithium non-aqueous electrolyte containing 1 M LiPF₆ as a lithium salt was added to a solvent including ethylene carbonate, dimethyl carbonate, and ethyl methyl carbonate mixed in a volumetric ratio of 20:40:40.

Comparative Example 2

A lithium secondary battery was manufactured in the same manner as in Example 1, except that a lithium non-aqueous electrolyte containing 1 M LiPF₆ as a lithium salt was added to a solvent including ethylene carbonate, dimethoxyethane, and digylm mixed in a volumetric ratio of 20:65:15.

Comparative Example 3

A lithium secondary battery was manufactured in the same manner as in Example 1, except that a lithium non-aqueous electrolyte containing 1 M LiPF₆ as a lithium salt was added to a solvent including ethylene carbonate, dimethoxyethane, and diglyme mixed in a volumetric ratio of 20:75:5.

Experimental Example 1

To measure lifespan characteristics of the lithium secondary batteries manufactured according to Example 1 and Comparative Example 1, a cycle of 1 C charge and 5 C discharge was carried out 400 times from 100% SOC to 0% SOC in a 45° C. chamber and then 1 C capacities were measured. Results are summarized in FIG. 2.

As shown in FIG. 2, it can be confirmed that the battery including the electrolyte containing diglyme exhibits superior lifespan characteristics, when compared with the battery including the existing carbonate based solvent.

Experimental Example 2

To measure lifespan characteristics of Examples 1 and 2 and Comparative Examples 2 and 3, 1 C capacities were measured in the same manner as in Experimental Example 1. Results are illustrated in FIG. 3.

As shown in FIG. 3, it can be confirmed that the battery in which diglyme was used in an amount of 40% or less exhibits superior lifespan characteristics.

Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.

INDUSTRIAL APPLICABILITY

As described above, since a secondary battery according to the present invention includes an electrolyte including predetermined amounts of a glyme based solvent and an ether based solvent, ionic conductivity may be improved and, as such, superior room- and low-temperature output characteristics may be exhibited.

When the electrolyte is used with lithium iron phosphate having an olivine crystal structure and amorphous carbon, internal resistance of a battery is reduced. Accordingly, rate characteristics and output characteristics of the battery are further improved and, thus, the battery may be suitably used in hybrid electric vehicles. 

1. An electrolyte for lithium secondary batteries comprising a lithium salt and a non-aqueous solvent, in which the non-aqueous solvent comprises an ether based solvent and a glyme based solvent, and a ratio of the ether based solvent to the glyme based solvent is 20:80 to 60:40 based on a total volume of the non-aqueous solvent.
 2. The electrolyte according to claim 1, wherein the glyme based solvent is at least one selected from the group consisting of ethylene glycol dimethyl ether (CH₃OCH₂CH₂OCH₃: monoglyme), diethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₂OCH₃: diglyme), diethylene glycol diethylether (C₂H₅(OCH₂CH₂)₂OC₂H₅), triethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₃OCH₃), and triethylene glycol diethylether (C₂H₅(OCH₂CH₂)₃OC₂H₅).
 3. The electrolyte according to claim 1, wherein the ether based solvent is at least one selected from tetrahydrofuran, 2-methyltetrahydrofuran, dimethyl ether, and dibutyl ether.
 4. The electrolyte according to claim 1, wherein the glyme based solvent is diethylene glycol dimethyl ether (CH₃(OCH₂CH₂)₂OCH₃: diglyme).
 5. The electrolyte according to claim 1, wherein a ratio of the ether based solvent to the glyme based solvent is 25:75 to 65:45 based on a total volume of the non-aqueous solvent.
 6. The electrolyte according to claim 1, wherein the electrolyte additionally comprises a carbonate based solvent.
 7. The electrolyte according to claim 6, wherein a ratio of a volume of a mixture of the glyme based solvent and the ether based solvent (A) to a volume of the carbonate based solvent (B) is 15:85 to 85:15 based on a total weight of the electrolyte.
 8. The electrolyte for lithium secondary batteries according to claim 6, wherein the carbonate based solvent is a cyclic carbonate, and the cyclic carbonate is at least one of ethylene carbonate (EC), propylene carbonate (PC), 1,2-butylene carbonate, 2,3-butylene carbonate, 1,2-pentylene carbonate, and 2,3-pentylene carbonate.
 9. The electrolyte for lithium secondary batteries according to claim 8, wherein the carbonate based solvent additionally comprises a linear carbonate, and the linear carbonate is at least one of dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), ethyl methyl carbonate (EMC), methyl propyl carbonate (MPC), and ethyl propyl carbonate (EPC), and the cyclic carbonate and the linear carbonate are mixed in a volumetric ratio of 1:4 to 4:1.
 10. The electrolyte for lithium secondary batteries according to claim 1, wherein the lithium salt is at least one selected from the group consisting of LiCl, LiBr, LiI, LiClO₄, LiBF₄, LiB₁₀Cl₁₀, LiPF₆, LiCF₃SO₃, LiCF₃CO₂, LiAsF₆, LiSbF₆, LiPF₆, LiAlCl₄, CH₃SO₃Li, CF₃SO₃Li, (CF₃SO₂)₂NLi, chloroborane lithium, lithium tetraphenyl borate, and imides, and a concentration of the lithium salt in the electrolyte is 0.5 to 3 M.
 11. A lithium secondary battery comprising the electrolyte for lithium secondary batteries according to claim
 1. 12. The lithium secondary battery according to claim 11, wherein the lithium secondary battery comprises: a cathode comprising a lithium metal phosphate according to Formula 1 below, as a cathode active material; and an anode comprising amorphous carbon, as an anode active material, Li_(1+a)M(PO_(4−b))X_(b)  (1) wherein M is at least one selected from metals of Groups II to XII, X is at least one selected from F, S and N, −0.5≦a≦+0.5, and 0≦b≦0.1.
 13. The lithium secondary battery according to claim 12, wherein the lithium metal phosphate is a lithium iron phosphate having an olivine crystal structure according to Formula 2 below: Li_(1+a)Fe_(1−x)M′_(x)(PO_(4−b))X_(b)  (2) wherein M′ is at least one selected from Al, Mg, Ni, Co, Mn, Ti, Ga, Cu, V, Nb, Zr, Ce, In, Zn, and Y, X is at least one selected from F, S, and N, and −0.5≦a≦+0.5, 0≦x≦0.5, and 0≦b≦0.1.
 14. The lithium secondary battery according to claim 13, wherein the lithium iron phosphate having the olivine crystal structure is LiFePO₄.
 15. The lithium secondary battery according to claim 14, wherein the lithium iron phosphate having the olivine crystal structure is coated with conductive carbon.
 16. The lithium secondary battery according to claim 12, wherein the amorphous carbon is hard carbon and/or soft carbon.
 17. A battery module comprising the lithium secondary battery according to claim 11 as a unit cell.
 18. A battery pack comprising the battery module according to claim
 17. 19. A device comprising the battery pack according to claim
 18. 20. The device according to claim 19, wherein the device is a hybrid electric vehicle, a plug-in hybrid electric vehicle, or an energy storage system. 